PETG Series
PLA Series
Functional Series
Flexible & Elastic Series
3D printing material is suitable for you
PETG Series
White
Grey
Black
High-Speed
PETG HF
50MPa
Tensile Strength
2412MPa
Tensile Modulus
75MPa
Flexural Strength
2205MPa
Flexural Modulus
8.2%
Elongation at Break
32J/m
Izod Impact(Notched)
75°C
Heat Deflection Temperature
78.5D
Hardness(Shore D)
White
Grey
Black
Matte Finish
Matte PETG
31MPa
Tensile Strength
1380MPa
Tensile Modulus
62MPa
Flexural Strength
2014MPa
Flexural Modulus
9.8%
Elongation at Break
60J/m
Izod Impact(Notched)
67°C
Heat Deflection Temperature
73.5D
Hardness(Shore D)
Black
10% carbon fiber content
PETG CF
56MPa
Tensile Strength
0.78kJ/m²
Notched Impact Strength
88MPa
Flexural Strength
2280MPa
Flexural Modulus
＜1%
Water Absorption
190-210℃
Melting Point
240-260℃
Nozzle Temperature
119R
Rockwell Hardness
PLA Series
White
Grey
Black
High-Speed
Standard PLA
56MPa
Tensile Strength
2700MPa
Tensile Modulus
76.7MPa
Flexural Strength
2100MPa
Flexural Modulus
4-6%
Elongation at Break
38J/m
Izod Impact(Notched)
53℃
Heat Deflection Temperature
81.D
Hardness(Shore D)
White
Grey
Black
Matte Finish
PLA Pro
49.6MPa
Tensile Strength
2000MPa
Tensile Modulus
68.9MPa
Flexural Strength
2933.6MPa
Flexural Modulus
10-13%
Elongation at Break
45-48J/m
Izod Impact(Notched)
53℃
Heat Deflection Temperature
78.D
Hardness(Shore D)
White
Grey
Black
10% carbon fiber content
Matte PLA
54.3MPa
Tensile Strength
2609.3MPa
Tensile Modulus
79.9MPa
Flexural Strength
2190.8MPa
Flexural Modulus
5-8%
Elongation at Break
35J/m
Izod Impact(Notched)
55℃
Heat Deflection Temperature
81.5
Hardness(Shore D)
Carbon fibre
Black
PLA-CF
56MPa
Tensile Strength
/
Tensile Modulus
89±4MPa
Flexural Strength
2570MPa
Flexural Modulus
9%
Elongation at Break
3.4KJ/m²
Izod Impact(Notched)
55℃
Heat Deflection Temperature
/
Hardness(Shore D)
Heat-resistant
White
High-Temp PLA
57MPa
Tensile Strength
2900MPa
Tensile Modulus
82.4MPa
Flexural Strength
2922.3MPa
Flexural Modulus
6.5%
Elongation at Break
24.8 KJ/m²
Izod Impact(Notched)
82°C
Heat Deflection Temperature
76.5D
Hardness(Shore D)
Shiny Like Chrome
Silk White
Silk Gold
Silk Silver
PLA Silk
41.9MPa
Tensile Strength
2510MPa
Tensile Modulus
63.8MPa
Flexural Strength
2400MPa
Flexural Modulus
12%
Elongation at Break
35J/m
Izod Impact(Notched)
53.9°C
Heat Deflection Temperature
80D
Hardness(Shore D)
Flexible & Elastic Series
Black
White
Clearr
Resilience
TPU 98A
36MPa
Tensile Strength
12MPa
Tensile Modulus
4.55MPa
Flexural Strength
/
Flexural Modulus
＞440%
Elongation at Break
125J/m
Izod Impact(Notched)
90℃
Heat Deflection Temperature
98A
Hardness(Shore D)
Black
White
Clearr
Resilience
TPU 95A
36MPa
Tensile Strength
11MPa
Tensile Modulus
4.55MPa
Flexural Strength
/
Flexural Modulus
＞370%
Elongation at Break
120KJ/m
Izod Impact(Notched)
110℃
Heat Deflection Temperature
95A
Hardness(Shore D)
Clearr
High Rebound Rate
PEBA 86A
30MPa
Tensile Strength
30MPa
Tensile Modulus
/
Flexural Strength
/
Flexural Modulus
600%
Elongation at Break
NB
Izod Impact(Notched)
0.5-0.7%
Heat Deflection Temperature
38D
Hardness(Shore D)
Functional Series
White
Black
Functional
ABS
50MPa
Tensile Strength
2412MPa
Tensile Modulus
75MPa
Flexural Strength
2205MPa
Flexural Modulus
8.2%
Elongation at Break
32J/m
Izod Impact(Notched)
75°C
Heat Deflection Temperature
78.5D
Hardness(Shore D)
White
Black
Functional
ASA
50MPa
Tensile Strength
2412MPa
Tensile Modulus
75MPa
Flexural Strength
2205MPa
Flexural Modulus
8.2%
Elongation at Break
32J/m
Izod Impact(Notched)
75°C
Heat Deflection Temperature
78.5D
Hardness(Shore D)